PENGARUH WAKTU PAPARAN RADIASI UV-C TERHADAP KARAKTERISTIK RAPAT ARUS DIFUSI ION PADA MEMBRAN KITOSAN
It has conducted research about the effects of UV-C irradiation to the current density of ion diffusion characteristics of chitosan membranes. A series of chitosan membranes with various ratios of components was used such as 1%, 2%, 3% and4%, the electrolyte solution was NaCl with various concentrat...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universitas Udayana
2016-02-01
|
| Series: | Buletin Fisika |
| Online Access: | https://ojs.unud.ac.id/index.php/buletinfisika/article/view/31329 |
| Summary: | It has conducted research about the effects of UV-C irradiation to the current density of ion diffusion characteristics of chitosan membranes. A series of chitosan membranes with various ratios of components was used such as 1%, 2%, 3% and4%, the electrolyte solution was NaCl with various concentration of 0.1 mM , 1 mM, 10 mM, 100 mM, and 1000 mM, and time exposure of 5, 15, 30, and 60 minutes. Ion transport processes were carried out in a cell membrane model which composed of two compartments, and the potential difference was measured using a pair of Activon AEP calomel electrodes. All the measurements were conducted at room temperature of about 28.1oC. The result showed that the current density increased with increasing some parameters e.g. the ratio of concentration of solution in both compartments (C1/C2), the amount of chitosan (1%, 2%, 3% and4%), and exposure time. |
|---|---|
| ISSN: | 1411-4690 2580-9733 |