Increase of austenitic ductile iron type D5S durability by high temperature pre-treatment
In the present work, a performance of ASTM A439 Austenitic Ductile Iron type D5S at high temperature in the oxidizing environment was investigated. The obtained results revealed that exposure at temperatures 800°C, 850°C, and 900°C resulted in relatively high mass gain and an extensive oxide scale s...