Effects of Transverse Crack on Chloride Ions Diffusion and Steel Bars Corrosion Behavior in Concrete under Electric Acceleration

Effects of Transverse Crack on Chloride Ions Diffusion and Steel Bars Corrosion Behavior in Concrete under Electric Acceleration

Cracks greatly impact the durability of concrete structures due to their influence on the migration of chloride ions and the corrosion process of steel bars. This study investigates the effects of transverse cracks on chloride diffusion and the corrosion behavior of two types of steel bars (low carb...

Full description

Bibliographic Details
Main Authors:	Fengyin Du, Zuquan Jin, Chuansheng Xiong, Yong Yu, Junfeng Fan
Format:	Article
Language:	English
Published:	MDPI AG 2019-08-01
Series:	Materials
Subjects:	crack width reinforced concrete chloride diffusion coefficient EIS electrochemical impedance spectroscopy
Online Access:	https://www.mdpi.com/1996-1944/12/15/2481

Similar Items

Effectiveness of inhibitors in increasing chloride threshold value for steel corrosion
by: Jin-xia Xu, et al.
Published: (2013-07-01)

Effect of Cracking on Corrosion of Steel in Concrete
by: Faiz Uddin Ahmed Shaikh
Published: (2018-01-01)

EFFECT OF PRESTRESSED FORCE AND SIZE OF REINFORCEMENT ON CORROSION CRACK WIDTH IN CONCRETE MEMBER
by: AGUS MARYOTO, et al.
Published: (2017-10-01)

A Novel Non-Destructive Sensing Technology for On-Site Corrosion Failure Evaluation of Coatings
by: Mian Hammad Nazir, et al.
Published: (2018-01-01)

Evaluation of the method of electrochemical extraction of chlorides ions for the rehabilitation of concrete structures with reinforcement corrosion problems
by: E. Monteiro, et al.
Published: (2003-12-01)

The Depth–Width Correlation for Shrinkage-Induced Cracks and Its Influence on Chloride Diffusion into Concrete
by: Hongguang Zhu, et al.
Published: (2020-06-01)

The Role of Electrochemical Impedance Spectroscopy in the Characterization of Electrodes and Devices for Energy Conversion and Storage
by: Magdić, K., et al.
Published: (2013-03-01)

Applicability of Diffuse Ultrasound to Evaluation of the Water Permeability and Chloride Ion Penetrability of Cracked Concrete
by: Eunjong Ahn, et al.
Published: (2018-11-01)

The electrochemical synthesis and corrosion behaviour of TiO2/poly(indole-co-aniline) multilayer coating: Experimental and theoretical approach
by: Serap Toprak Döşlü, et al.
Published: (2018-01-01)

Susceptibility to Stress Corrosion and Crack Initiation and Propagation of 7A04 Aluminum Alloys
by: DU Juan, et al.
Published: (2018-04-01)

Corrosion behavior of as-cast binary Mg-Bi alloys in Hank's solution
by: Wei-li Cheng, et al.
Published: (2015-11-01)

Experimental investigation of crack width variation along the concrete cover depth in reinforced concrete specimens with ribbed bars and smooth bars
by: Chavin N. Naotunna, et al.
Published: (2021-12-01)

Cracks width-corrosion rate correlation on the durability of reinforced concrete in a very high aggressiveness tropical marine environment
by: Andrés Antonio Torres Acosta, et al.
Published: (2018-08-01)

Modeling the Time-to Corrosion Cracking of the Cover Concrete in Chloride Contaminated Reinforced Concrete Structures
by: Liu, Youping
Published: (2014)

Improving pitting corrosion resistance of the commercial titanium through graphene oxide-titanium oxide composite
by: Talal A. Aljohani, et al.
Published: (2021-06-01)

Corrosion Protection Evaluation of Mild Steel: The Role of Hybrid Materials Loaded with Inhibitors
by: Ioannis A. Kartsonakis, et al.
Published: (2020-09-01)

Analysis of methods for calculating the width of normal cracks in reinforced concrete structures
by: Vidmantas Jokūbaitis, et al.
Published: (2009-05-01)

A Numerical Study on Chloride Diffusion in Cracked Concrete
by: Qiannan Wang, et al.
Published: (2021-06-01)

Crack Width Estimation of Mortar Specimen Using Gas Diffusion Experiment
by: Do-Keun Lee, et al.
Published: (2019-09-01)

Effect of Reinforced Concrete Cracking on Chloride Ion Penetration
by: Yuan Chao, et al.
Published: (2015-01-01)

Concrete Corrosion Cracking and Transverse Bar Strain Behavior in a Reinforced Concrete Column under Simulated Marine Conditions
by: Gyeongcheol Choe, et al.
Published: (2020-03-01)

Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
by: R. K. Singh Raman, et al.
Published: (2014-12-01)

Experimental Evaluation of the Bond Dependent Coefficient and Parameters which Influence Crack Width in GFRP Reinforced Concrete
by: McCallum, Brittany
Published: (2013)

Crack width evaluation for flexural RC members
by: Said M. Allam, et al.
Published: (2012-09-01)

Corrosion of reinforcing bars embedded in alkali-activated slag concrete subjected to chloride attack
by: William Aperador Chaparro, et al.
Published: (2012-02-01)

Influence of the Alkaline Reserve of Chloride-Contaminated Mortars on the 6-Year Corrosion Behavior of Corrugated UNS S32304 and S32001 Stainless Steels
by: Asunción Bautista, et al.
Published: (2019-06-01)

Minimum Reinforcement for Crack Width Control in RC Tensile Elements
by: Knauff M., et al.
Published: (2019-03-01)

The analysis of crack width in flexural concrete members reinforced with polymer composite bars
by: Ilshat T. Mirsayapov, et al.
Published: (2020-12-01)

Stress Corrosion Cracking Detection of Sensitized Stainless Steel 304 in Chloride Media by Using Electrochemical Impedance Spectroscopy (EIS)
by: J. Neshati, et al.
Published: (2012-01-01)

An Impedance Sensor in Detection of Immunoglobulin G with Interdigitated Electrodes on Flexible Substrate
by: Kai Jin, et al.
Published: (2020-06-01)

Chemical properties of hydroxyapatite deposited through electrophoretic process on different sandblasted samples
by: Gradinariu Irina, et al.
Published: (2014-12-01)

Characterization of bornite (Cu5FeS4) electrodes in the presence of the bacterium Acidithiobacillus ferrooxidans
by: Bevilaqua Denise, et al.
Published: (2003-01-01)

Analysis of Crack Width Development in Reinforced Concrete Beams
by: Barbara Goszczyńska, et al.
Published: (2021-06-01)

Modelling of Behavior for Inhibition Corrosion of Bronze Using Artificial Neural Network (ANN)
by: D. Elusaí Millán-Ocampo, et al.
Published: (2018-05-01)

A study on corrosion of X80 steel in a simulated tidal zone
by: Xiaobao Zhou, et al.
Published: (2021-05-01)

Study on corrosion inhibition performance of 4,5-diamino-6-hydroxy-2-mercapto-pyrimidine film on copper against NaCl solution
by: LIU Zequn, et al.
Published: (2019-04-01)

Surface treated cp-titanium for biomedical applications : a combined corrosion, tribocorrosion and biological approach
by: Yang, Yaqin
Published: (2014)

Anti-Corrosive Properties of an Effective Guar Gum Grafted 2-Acrylamido-2-Methylpropanesulfonic Acid (GG-AMPS) Coating on Copper in a 3.5% NaCl Solution
by: Ambrish Singh, et al.
Published: (2020-03-01)

Uncertainty in Crack width Estimates According to Fib Model Code 2010
by: Mlčoch Jan, et al.
Published: (2017-06-01)

Diagnostics of Large Non-Conductive Anti-Corrosion Coatings on Steel Structures by Means of Electrochemical Impedance Spectroscopy
by: Tomasz Jaśniok, et al.
Published: (2021-07-01)

Cannot write session to /tmp/vufind_sessions/sess_o0fqnhau8cn9o86ds6iqvpu5i8