Development of La3+ Doped CeO2 Thick Film Humidity Sensors
The humidity sensitive characteristics of the sensor fabricated from 10 mol% La2O3 doped CeO2 nanopowders with particle size 17.26 nm synthesized via hydrothermal method were investigated at different frequencies. It was found that the sensor shows high humidity sensitivity, rapid response-recovery...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2014-01-01
|
| Series: | Abstract and Applied Analysis |
| Online Access: | http://dx.doi.org/10.1155/2014/297632 |
| Summary: | The humidity sensitive characteristics of the sensor fabricated from 10 mol% La2O3 doped CeO2 nanopowders with particle size 17.26 nm synthesized via hydrothermal method were investigated at different frequencies. It was found that the sensor shows high humidity sensitivity, rapid response-recovery characteristics, and narrow hysteresis loop at 100 Hz in the relative humidity range from 11% to 95%. The impedance of the sensor decreases by about five orders of magnitude as relative humidity increases. The maximum humidity hysteresis is about 6% RH, and the response and recovery time is 12 and 13 s, respectively. These results indicate that the nanosized La2O3 doped CeO2 powder has potential application as high-performance humidity sensor. |
|---|---|
| ISSN: | 1085-3375 1687-0409 |