LOW TEMPERATURE PHOSPHORIC ACID TREATMENT OF ZINC OXIDE FOR NOBEL WHITE PIGMENTS
Zinc oxide that has the photocatalytic activity is used as white pigment for cosmetics. A certain degree of sebum on the skin is decomposed by the ultraviolet radiation in sunlight. In this work, zinc oxide was shaken with phosphoric acid to synthesize a white pigment for cosmetics. Zinc oxide was s...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Chemistry and Technology, Prague
2019-07-01
|
| Series: | Ceramics-Silikáty |
| Subjects: | |
| Online Access: |
http://www.ceramics-silikaty.cz/index.php?page=cs_detail_doi&id=1277
|
| Summary: | Zinc oxide that has the photocatalytic activity is used as white pigment for cosmetics. A certain degree of sebum on the skin is decomposed by the ultraviolet radiation in sunlight. In this work, zinc oxide was shaken with phosphoric acid to synthesize a white pigment for cosmetics. Zinc oxide was set with 0.1 mol/L of phosphoric acid at P/Zn = 1/1 and 1/2, and then shaking in water at 30, 40, 50°C for 1, 3, 6 hours. The chemical composition, powder properties, photocatalytic activity, color phase, and smoothness of the obtained powder were studied. The P/Zn ratio in preparation had influence on the reaction between phosphoric acid and zinc oxide. The photocatalytic activity of zinc oxide was inhibited by phosphoric acid treatment. The treated samples at 50°C had enough high reflectance at the visible light region. |
|---|---|
| ISSN: | 0862-5468 1804-5847 |