Improving the Properties of Laser-Welded Al–Zn–Mg–Cu Alloy Joints by Aging and Double-Sided Ultrasonic Impact Compound Treatment

• Main Authors: Furong Chen, Chenghao Liu
• Format: Article
• Language: English
• Published: MDPI AG 2021-05-01
• Series: Materials
• Subjects: 7075 aluminum alloy; welded joint; aging; ultrasonic impact treatment; microstructure; EBSD
• Online Access: https://www.mdpi.com/1996-1944/14/11/2742

To improve the loose structure and serious porosity of (Al–Zn–Mg–Cu) 7075 aluminum alloy laser-welded joints, aging treatment, double-sided ultrasonic impact treatment (DSUIT), and a combination of aging and DSUIT (A–DSUIT) were used to treat joints. In this experiment, the mechanism of A–DSUIT on the microstructure and properties of welded joints was analyzed. The microstructure of the welded joints was observed using optical microscopy, scanning electron microscopy, and electron backscatter diffraction (EBSD). The hardness and tensile properties of the welded components under the different processes were examined via Vickers hardness test and a universal tensile testing machine. The results showed that, after the aging treatment, the dendritic structure of the welded joints transformed into an equiaxed crystal structure. Moreover, the residual tensile stress generated in the welding process was weakened, and the hardness and tensile strength were significantly improved. After DSUIT, a plastic deformation layer of a certain thickness was generated from the surface downward, and the residual compressive stress was introduced to a certain depth of the joint. However, the weld zone unaffected by DSUIT still exhibited residual tensile stress. The inner microhardness of the joint surface improved; the impact surface hardness was the largest and gradually decreased inward to the weld zone base metal hardness, with a small improvement in the tensile strength. Compared with the single treatment process, the microstructural and mechanical properties of the welded joint after A–DSUIT were comprehensively improved. The microhardness and tensile strength of the welded joint reached 200 HV and 615 MPa, respectively, for an increase of 45.8% and 61.8%, respectively. Observation of the fractures of the tensile specimens under the different treatment processes showed that the fractures before the aging treatment were mainly ductile fractures while those after were mainly brittle fractures. After DSUIT of the welded joints, a clear and dense plastic deformation layer was observed in the fracture of the tensile specimens and effectively improved the tensile properties of the welded joints. Under the EBSD characterization, the larger the residual compressive stress near the ultrasonic impact surface, the smaller the grain diameter and misorientation angle, and the lower the texture strength. Finally, after A–DSUIT, the hardness and tensile properties improved the most.