Surface-Enhanced Raman Scattering Study of Silver Nanoparticles Prepared by Using MC as a Template
A good Ag-based SERS substrate has been prepared by one-pot reaction using methyl cellulose as a template. Effects of methyl cellulose concentration, silver ammonia chloride solution concentration, reaction duration, and reducing agent on silver nanoparticles were discussed in this paper. The perfor...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2013-01-01
|
| Series: | Journal of Nanomaterials |
| Online Access: | http://dx.doi.org/10.1155/2013/984831 |
| Summary: | A good Ag-based SERS substrate has been prepared by one-pot reaction using methyl cellulose as a template. Effects of methyl cellulose concentration, silver ammonia chloride solution concentration, reaction duration, and reducing agent on silver nanoparticles were discussed in this paper. The performance of the obtained Ag nanoparticles was characterized by UV-visible spectroscopy, transmission electron microscopy, and surface-enhanced Raman spectroscopy. Results show that the reducing agent plays a crucial role in the performance of silver nanoparticles. Optimum preparation conditions of synthesis of SERS substrates were as follows: 10 mM silver ammonia chloride and 0.2% MC at 75°C, reducing in 0.2% reducing agent at 120 min. TEM studies reveal that particles are mostly spherical and rod in shape with an average size of 80 nm. Silver nanoparticles prepared with MC as a template have been shown to provide strong SERS enhancement signals of R6G, which can be used as a good Ag-based SERS substrate in the analytical environment for routine measurements. |
|---|---|
| ISSN: | 1687-4110 1687-4129 |