A new biocompatible delivery scaffold containing heparin and bone morphogenetic protein 2
Silicon-substituted calcium phosphate (Si-CaP) was developed in our laboratory as a biomaterial for delivery in bone tissue engineering. It was fabricated as a 3D-construct of scaffolds using chitosan-trisodium polyphosphate (TPP) cross-linked networks. In this study, heparin was covalently bonded t...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Sciendo
2016-09-01
|
| Series: | Acta Pharmaceutica |
| Subjects: | |
| Online Access: | https://doi.org/10.1515/acph-2016-0026 |
| Summary: | Silicon-substituted calcium phosphate (Si-CaP) was developed in our laboratory as a biomaterial for delivery in bone tissue engineering. It was fabricated as a 3D-construct of scaffolds using chitosan-trisodium polyphosphate (TPP) cross-linked networks. In this study, heparin was covalently bonded to the residual -NH2 groups of chitosan on the scaffold applying carbodiimide chemistry. Bonded heparin was not leached away from scaffold surfaces upon vigorous washing or extended storage. Recombinant human bone morphogenetic protein 2 (rhBMP-2) was bound to conjugated scaffolds by ionic interactions between the negatively charged SO42- clusters of heparin and positively charged amino acids of rhBMP-2. The resulting scaffolds were inspected for bone regenerative capacity by subcutaneous implanting in rats. Histological observation and mineralization assay were performed after 4 weeks of implantation. Results from both in vitro and in vivo experiments suggest the potential of the developed scaffolds for bone tissue engineering applications in the future. |
|---|---|
| ISSN: | 1846-9558 |