Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo

Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo

Metallographic examinations and mechanical tests were carried out on the ductile iron with additions of Ni, Cu and Mo in as-cast state and after austempering. TTT and CCT diagrams were plotted. The heat treatment was performed in six different variants. Studies included qualitative assessment of the...

Full description

Bibliographic Details
Main Authors: Mrzygłód B., Kowalski A., Olejarczyk-Wożenska I., Adrian H., Głowacki M., Opaliński A.
Format: Article
Language:English
Published: Polish Academy of Sciences 2015-09-01
Series:Archives of Metallurgy and Materials
Subjects:
ductile iron
heat treatment
the microstructure of ADI
ADI mechanical properties
Online Access:http://www.degruyter.com/view/j/amm.2015.60.issue-3/amm-2015-0330/amm-2015-0330.xml?format=INT
id doaj-471c5e9854b0442f87120ef60a5743a8
record_format Article
spelling doaj-471c5e9854b0442f87120ef60a5743a82020-11-25T03:12:09ZengPolish Academy of SciencesArchives of Metallurgy and Materials2300-19092015-09-016031941194810.1515/amm-2015-0330amm-2015-0330Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, MoMrzygłód B.0Kowalski A.1Olejarczyk-Wożenska I.2Adrian H.3Głowacki M.4Opaliński A.5 AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, AL. A.MICKIEWICZA 30 30-059 KRAKOW, POLAND FOUNDRY RESEARCH INSTITUTE, 73 ZAKOPIAŃSKA STR., 30-418 KRAKOW, POLANAA AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, AL. A.MICKIEWICZA 30 30-059 KRAKOW, POLAND AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, AL. A.MICKIEWICZA 30 30-059 KRAKOW, POLAND AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, AL. A.MICKIEWICZA 30 30-059 KRAKOW, POLAND AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, AL. A.MICKIEWICZA 30 30-059 KRAKOW, POLANDMetallographic examinations and mechanical tests were carried out on the ductile iron with additions of Ni, Cu and Mo in as-cast state and after austempering. TTT and CCT diagrams were plotted. The heat treatment was performed in six different variants. Studies included qualitative assessment of the microstructure and testing of mechanical properties such as R0,2, Rm, A, Z, HRC, KC. An analysis of the obtained results was also presented.http://www.degruyter.com/view/j/amm.2015.60.issue-3/amm-2015-0330/amm-2015-0330.xml?format=INTductile ironheat treatmentthe microstructure of ADIADI mechanical properties
collection DOAJ
language English
format Article
sources DOAJ
author Mrzygłód B.
Kowalski A.
Olejarczyk-Wożenska I.
Adrian H.
Głowacki M.
Opaliński A.
spellingShingle Mrzygłód B.
Kowalski A.
Olejarczyk-Wożenska I.
Adrian H.
Głowacki M.
Opaliński A.
Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo
Archives of Metallurgy and Materials
ductile iron
heat treatment
the microstructure of ADI
ADI mechanical properties
author_facet Mrzygłód B.
Kowalski A.
Olejarczyk-Wożenska I.
Adrian H.
Głowacki M.
Opaliński A.
author_sort Mrzygłód B.
title Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo
title_short Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo
title_full Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo
title_fullStr Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo
title_full_unstemmed Effect Of Heat Treatment Parameters On The Formation Of ADI Microstructure With Additions Of Ni, Cu, Mo
title_sort effect of heat treatment parameters on the formation of adi microstructure with additions of ni, cu, mo
publisher Polish Academy of Sciences
series Archives of Metallurgy and Materials
issn 2300-1909
publishDate 2015-09-01
description Metallographic examinations and mechanical tests were carried out on the ductile iron with additions of Ni, Cu and Mo in as-cast state and after austempering. TTT and CCT diagrams were plotted. The heat treatment was performed in six different variants. Studies included qualitative assessment of the microstructure and testing of mechanical properties such as R0,2, Rm, A, Z, HRC, KC. An analysis of the obtained results was also presented.
topic ductile iron
heat treatment
the microstructure of ADI
ADI mechanical properties
url http://www.degruyter.com/view/j/amm.2015.60.issue-3/amm-2015-0330/amm-2015-0330.xml?format=INT
work_keys_str_mv AT mrzygłodb effectofheattreatmentparametersontheformationofadimicrostructurewithadditionsofnicumo
AT kowalskia effectofheattreatmentparametersontheformationofadimicrostructurewithadditionsofnicumo
AT olejarczykwozenskai effectofheattreatmentparametersontheformationofadimicrostructurewithadditionsofnicumo
AT adrianh effectofheattreatmentparametersontheformationofadimicrostructurewithadditionsofnicumo
AT głowackim effectofheattreatmentparametersontheformationofadimicrostructurewithadditionsofnicumo
AT opalinskia effectofheattreatmentparametersontheformationofadimicrostructurewithadditionsofnicumo
_version_ 1724651345254809600

Similar Items