| Summary: | Al-xFe-La alloys (x = 0.07, 0.1, 0.2) for aluminum current collectors of lithium-ion batteries were prepared and the microstructure of Al-0.07Fe-0.07La, Al-0.1Fe-0.07La and Al-0.2Fe-0.07La aluminum alloys were observed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS). The experimental results showed that with the increase of Fe content, the size of the second phases in Al-xFe-0.07La alloys became finer and more dispersed and that the microstructure of the alloy had improved. The strength and corrosion resistance of Al-xFe-La alloys were studied by tensile tests and electrochemical tests and the morphological investigations of samples were also conducted by SEM and EDS. With the increase of Fe content, the strength and corrosion resistance of Al-xFe-La alloys became better. Compared to Al-0.07Fe-0.07La alloy, the yield strength and tensile strength of the Al-0.2Fe-0.07La alloy increased by 51.19% and 58.48% respectively, and the elongation increased by 88.41%. Moreover, Al-0.2Fe-0.07La alloy had much more positive corrosion potential and much smaller corrosion current than those of Al-0.07Fe-0.07La alloy.
|
|---|