High pressure sintering of TiB2 ceramics at different temperatures

• Main Authors: Andrei V. Kapylou, Vladimir S. Urbanovich, Vladimir A. Kukareko
• Format: Article
• Language: English
• Published: University of Novi Sad 2008-06-01
• Series: Processing and Application of Ceramics
• Subjects: Titanium diboride; High-pressure sintering
• Online Access: http://www.tf.uns.ac.rs/publikacije/PAC/pdf/15%20PAC%2002.pdf

In this paper the effect of high-pressure sintering (HPS) temperature on the microstructure, physical and mechanical properties of TiB2 ceramics has been investigated. Initial TiB2 powder with the average particle size of 5 μm was sintered in a modifi ed high-pressure anvil-type apparatus under static pressure of 4 GPa in the temperature range of 1400–1800°C. It is shown that HPS allows preparing full-dense TiB2 ceramics with fi ne-grained structure. The density of samples rises with increasing the sintering temperature up to 1800°C while the maximal microhardness is observed on samples prepared in the temperature range of 1500–1600°C. XRD analysis has shown that this fact is connected with an increase of the level of internal stresses in these samples.