Obtaining porous quartz sand–glass composite for production of diffusers for water aeration
Quartz sand with granulation 0.125 ÷ 0.063 mm and 30 wt% waste TV glass were used for preparation of glass ceramic composites with controlled porosity of 24.4 ± 1.5 %, and interconnected pores with size of 250–400 μm. The production of this composite was realized at 950 ºC/2h. This composite possess...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Society of Chemists and Technologists of Macedonia
2008-06-01
|
| Series: | Macedonian Journal of Chemistry and Chemical Engineering |
| Subjects: | |
| Online Access: | https://mjcce.org.mk/index.php/MJCCE/article/view/244 |
| Summary: | Quartz sand with granulation 0.125 ÷ 0.063 mm and 30 wt% waste TV glass were used for preparation of glass ceramic composites with controlled porosity of 24.4 ± 1.5 %, and interconnected pores with size of 250–400 μm. The production of this composite was realized at 950 ºC/2h. This composite possesses E-modulus and bending strength of 12.0 ± 1.2 GPa and 16.1 ± 1.4 MPa, respectively. The permeability and form coefficient of this porous composite were K0 = 3.22 Da and C0 = 3.92·106 m–1, respectively. This porous composite represents a potential material for production of air diffusers for water aeration. |
|---|---|
| ISSN: | 1857-5552 1857-5625 |