| Summary: | The waterproof and thermal insulation property of foamed concrete is very important. In this study, the ultrafine fly ash (UFA)-based superhydrophobic composite coating was applied onto foam concrete. The UFA-based base coating that closely adhered to the concrete initially improved the waterproofness of the test block, and the silane coupling agent-modified UFA-based surface coating further achieved superhydrophobicity. The UFA on the coating surface and the asperities on the surface jointly formed a lotus leaf-like rough micro–nanostructure. The 154.34° water drop contact angle and 2.41° sliding angle on No. 5 coating were reached, indicating that it was a superhydrophobic surface. The water absorption ratios of the composite coating block were 1.87% and 16.6% at 4 h and 7 days, which were reduced by 97% and 75% in comparison with the original foam concrete. The compressive strength and heat conductivity coefficient after soaking for 4 h of the composite coating block were higher than 4.0 MPa and 0.225 W·m<sup>−1</sup>·K<sup>−1</sup>, respectively. The UFA-based superhydrophobic composite coating proposed in this study and applied onto foam concrete is simple and cheap, requires no precise instrument, and can be applied in a large area.
|
|---|