Dependence Of The Structure And Magnetic Properties Of Cast Plate-Shaped Nd60Fe30Al10 Samples On Their Thickness

• Main Authors: Michalski B., Kaszuwara W., Latuch J., Pawlik P.
• Format: Article
• Language: English
• Published: Polish Academy of Sciences 2015-09-01
• Series: Archives of Metallurgy and Materials
• Subjects: hard magnetic materials; Nd-Fe-Al alloys; rapid quenching
• Online Access: http://www.degruyter.com/view/j/amm.2015.60.issue-3/amm-2015-0283/amm-2015-0283.xml?format=INT

The hard magnetic Nd-Fe-Al alloys are inferior to Nd-Fe-B magnets as far as the magnetic properties are concerned, but their great advantage is that they need no additional annealing to achieve good magnetic properties. These properties depend on the cooling rate from the melting state, and on the thickness of the sample - the best values are achieved at the quenching rates at which the samples have a thickness of 0.3-2 mm. The present study is concerned with the correlation between the magnetic properties of the plate-shaped Nd60Fe30Al10 samples and their size - thickness. Two casting ways: with the melt stream perpendicular direction and parallel to the surface of the plates were used. The plates were produced by pressure casting and suction casting. The studies have shown that the cooling rates depends on local propagation on liquid metal in the mold resulting in heterogeneity of structure and properties.