Photodegradation of Methylene Blue by TiO2-Fe3O4-Bentonite Magnetic Nanocomposite
Fe3O4-bentonite nanoparticles have been prepared by a coprecipitation technique under a nitrogen atmosphere. An aqueous suspension of bentonite was first modified with FeCl2 and FeCl3. TiO2 was then loaded onto the surface of the Fe3O4-bentonite by a sol-gel method. After sufficient drying, the coll...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2015-01-01
|
| Series: | International Journal of Photoenergy |
| Online Access: | http://dx.doi.org/10.1155/2015/591428 |
| Summary: | Fe3O4-bentonite nanoparticles have been prepared by a coprecipitation technique under a nitrogen atmosphere. An aqueous suspension of bentonite was first modified with FeCl2 and FeCl3. TiO2 was then loaded onto the surface of the Fe3O4-bentonite by a sol-gel method. After sufficient drying, the colloidal solution was placed in a muffle furnace at 773 K to obtain the TiO2-Fe3O4-bentonite composite. The material has been characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis, and vibrating sample magnetometry (VSM). Morphological observation showed that Fe3O4 and TiO2 nanoparticles had been adsorbed on the surface of bentonite nanoneedles. The material was then applied for the photodegradation of the azo dye methylene blue (MB). It was found that the removal efficiency of MB exceeded 90% under UV illumination, and that only a 20% mass loss was incurred after six cycles. The composite material thus showed good photocatalytic performance and recycling properties. |
|---|---|
| ISSN: | 1110-662X 1687-529X |