Improved mechanical properties of dense β-Si3N4 ceramics fabricated by spark plasma sintering with Al2O3-YSZ additives

• Main Authors: Yang Li, Weiqin Ao, Jihua Gao, Chaohua Zhang, Fusheng Liu, Yong Du
• Format: Article
• Language: English
• Published: University of Novi Sad 2018-12-01
• Series: Processing and Application of Ceramics
• Subjects: Si3N4; spark plasma sintering; sintering additives; mechanical properties; microstructure
• Online Access: http://www.tf.uns.ac.rs/publikacije/PAC/pdf/PAC%2042%2002.pdf
• ISSN: 1820-6131; 2406-1034

In this work the influence of sintering conditions on structure and mechanical properties of Si3N4 ceramics was investigated. Nearly full dense β-Si3N4 ceramics with excellent mechanical properties and interlock microstructure of elongated grains was fabricated using Al2O3 and yttria-stabilized zirconia (YSZ with 3 mol% Y2O3) as sintering additives by spark plasma sintering (SPS) at relatively low temperature of 1600 °C for 15 min. X-ray diffraction analysis shows that the SPSed sample is pure β-Si3N4 phase without any secondary crystalline phase. The elements Al, Zr, Y and O of the additive can diffuse into Si3N4 lattice forming β-Si3N4-based solid solution. The residual additive formed an amorphous phase at the β-Si3N4 grain boundaries. The β-Si3N4 ceramics obtained by SPS using 6.0 wt.% Al2O3 and 6.0 wt.% YSZ as additives shows interlock elongated β-Si3N4 grains of 500 nm in width and 3000 nm in length, high density of 3.29 g/cm3, Vickers hardness of 16.15 GPa and high fracture toughness KIC of 6.75 MPa m1/2 .