| Summary: | In recent years, partial replacement of cement with bagasse ash has been given attention for construction application due to its pozzolanic characteristics. Sugarcane bagasse ash and fine bagasse particles are abundant byproducts of the sugar industries and are disposed of in landfills. Our study presents the effect of burning bagasse at different temperatures (300 °C and 600 °C) on the compressive strength and physical properties of bagasse ash-blended mortars. Experimental results have revealed that bagasse produced more amorphous silica with very low carbon contents when it was burned at 600 °C/2 h. The compressive strength of mortar was improved when 5% bagasse ash replaced ordinary portland cement (OPC) at early curing ages. The addition of 10% bagasse ash cement also increased the compressive strength of mortars at 14 and 28 days of curing. However, none of the bagasse ash-blended portland pozzolana cement (PPC) mortars have shown improvement on compressive strength with the addition of bagasse ash. Characterization of bagasse ash was done using XRD, DTA-TGA, SEM, and atomic absorption spectrometry. Moreover, durability of mortars was checked by measuring water absorption and apparent porosity for bagasse ash-blended mortars.
|
|---|