| Summary: | Polyethylene glycol (PEG) non-covalent-functionalized multi-walled carbon nanotubes (MWCNT) membrane were prepared by vacuum filtration. The dispersion and stability of MWCNT non-covalent functionalized with PEG were all improved. TEM characterization and XPS quantitative analysis proved that the use of PEG to non-covalent functionalize MWCNT was successful. SEM image analysis confirmed that the pore size of PEG–MWCNT membrane was more concentrated and distributed in a narrower range of diameter. Contact angle measurement demonstrated that PEG non-covalent functionalization greatly enhanced the hydrophilicity of MWCNT membranes. The results of pure water flux showed that the PEG–MWCNT membranes could be categorized into low pressure membrane. PEG-MWCNT membrane had a better effect on the removal of humic acid (HA) and a lower TMP growth rate compared with a commercial 0.01-μm PVDF ultrafiltration membrane. During the filtration of bovine serum albumin (BSA), the antifouling ability of PEG-MWCNT membranes were obviously better than the raw MWCNT membranes. The TMP recovery rate of PEG–MWCNT membrane after cross flushing was 79.4%, while that of raw MWCNT–<sub>COOH</sub> and MWCNT membrane were only 14.9% and 28.3%, respectively. PEG non-covalent functionalization improved the antifouling ability of the raw MWCNT membranes and reduced the irreversible fouling, which effectively prolonged the service life of MWCNT membrane.
|
|---|