| Summary: | The recovery and leaching kinetics of lithium from lepidolite by sulfuric acid method were investigated in this study, and a new method of nanofiltration to separate Al/Li from lepidolite leaching solution was coupled. The results indicated the optimal conditions about leaching lithium from lepidolite: leaching at 433 K for 4 h with the agitation rate of 120 r min<sup>−1</sup>, sulfuric acid concentration of 60 wt%, liquid-solid mass ratio of 2.5:1, under which the Li yield could reach at 97%. The kinetics observations revealed that the leaching process was controlled by the hybrid control of solid product layer diffusion and the chemical reaction, and dominated by chemical reaction step, which improved the conclusion of single-step control in the previous literature. A successful attempt was made to couple nanofiltration separation with sulfuric acid extraction of lithium, and DK membrane was used to separate Al/Li from lepidolite leaching solution. DK membrane has shown excellent retention of Al<sup>3+</sup> and Ca<sup>2+</sup> and also can effectively permeate Li<sup>+</sup>, which may bring a new inspiration for lithium extraction from lepidolite in the future.
|
|---|