Electronic tricroscopic examination of the structure of the Ti-50.2 at. % Ni alloy
The method of electron-microscopic analysis investigated the structure of the alloy Ti-50.2 at % Ni at different stages of dissolution; low-temperature thermomechanical treatment (LTTT), post-deformation edgy (PDE), and recrystallization. The microstructure of B2-austenite, which is formed in the pr...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2021-01-01
|
| Series: | E3S Web of Conferences |
| Online Access: | https://www.e3s-conferences.org/articles/e3sconf/pdf/2021/40/e3sconf_conmechydro2021_05047.pdf |
| Summary: | The method of electron-microscopic analysis investigated the structure of the alloy Ti-50.2 at % Ni at different stages of dissolution; low-temperature thermomechanical treatment (LTTT), post-deformation edgy (PDE), and recrystallization. The microstructure of B2-austenite, which is formed in the process of incoordination, was also investigated, including in the conditions of isothermic burning of the original recrystallized structure. |
|---|---|
| ISSN: | 2267-1242 |