Nd3-xBixFe4GaO12 (x = 2, 2.5) films on glass substrates prepared by MOD method
We studied Nd3-XBiXFe4GaO12 films to obtain perpendicular magnetic anisotropy as well as large Faraday effect. NdBi2Fe4GaO12 (Bi2:NIGG) and Nd0.5Bi2.5Fe4GaO12 (Bi2.5:NIGG) films were obtained on Nd2BiFe4GaO12 (Bi1:NIGG) layer prepared on glass substrates by metal-organic decomposition (MOD) method....
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2014-07-01
|
| Series: | EPJ Web of Conferences |
| Online Access: | http://dx.doi.org/10.1051/epjconf/20147505009 |
| Summary: | We studied Nd3-XBiXFe4GaO12 films to obtain perpendicular magnetic anisotropy as well as large Faraday effect. NdBi2Fe4GaO12 (Bi2:NIGG) and Nd0.5Bi2.5Fe4GaO12 (Bi2.5:NIGG) films were obtained on Nd2BiFe4GaO12 (Bi1:NIGG) layer prepared on glass substrates by metal-organic decomposition (MOD) method. Bi2:NIGG and Bi2.5:NIGG films showed large Faraday rotation angles of 7.5 and 10.5 degree/µm, at a wavelength of 520 nm, respectively. Those films have perpendicular magnetic anisotropy with a coercivity of 350 Oe and a saturation magnetic field of 730 Oe.
|
|---|---|
| ISSN: | 2100-014X |