Effect of Staining and Bleaching on Surface Roughness of Different Nano Hybrid Resin Composite Materials

• Main Authors: Zahraa Sabah Abdulwahhab, Emad F. Alkhalidi
• Format: Article
• Language: Arabic
• Published: University of Mosul, College of Dentistry 2021-03-01
• Series: Al-Rafidain Dental Journal
• Subjects: resin composite; staining; bleaching; hydrogen peroxide; surface roughness; stylus profilometer.
• Online Access: https://rden.mosuljournals.com/pdf_167804_235b766dbb51130a0c5d1612a5b390f0.html

Aims: The purpose of this study was to evaluate the effects of staining by coffee and In-office bleaching by 30% hydrogen peroxide on surface roughness of two different Nano-Hybrid resin composite materials. Materials and Methods: In this in vitro experimental study, 32disc samples were fabricated from each type of the Nano-Hybrid resin composite materials, each sample measured 5 mm in diameter and 2 mm in height. The samples for each composite group were then sub-divided randomly into four sub-groups (n=8). In control sub-groups, samples were stored in artificial saliva at 37°C for 1 week. Samples of Staining sub-groups were stored in a coffee solution for 48h at 37°C. Samples of Staining Bleaching sub-groups were stained in a coffee solution for 48 h at 37°C then bleached with 30% H2O2. Samples of Bleaching sub-groups were bleached with 30% H2O2. The surface roughness measurements were taken for all samples of each sub-group; the measurements for control sub-groups considered as baseline data. Results: The surface roughness measurements of all sub-groups for both tested materials didn’t exceed the critical value (Ra< 0.2 μm) with no significant difference among all sub-groups (P >0.05). Conclusion: Surface roughness of the two tested Nano-Hybrid resin composite materials were neither influenced by coffee staining nor by in-office bleaching with 30% H2O2.