| Summary: | The influences of processing parameters such as volumetric energy density (ε) and, particularly, defocusing amount (DA) on densification, microstructure, tensile property, and hardness of the as-printed dense AlSi10Mg alloy by selective laser melting (SLM) were studied systematically. The molten pool boundaries (MPBs) were found overwhelmingly at regular and complex spatial topological structures affected by DA value to exist in two forms, while the “layer–layer” MPB overlay mutually and the “track–track” MPBs intersect to form acute angles with each other. The microstructure of MPBs exhibits a coarse grain zone near the MPBs and the characteristics of segregation of nonmetallic elements (O, Si) where the crack easily happened. The DA value (−2 to 2 mm) affected both the density and the tensile mechanical properties. High tensile strength (456 ± 14 MPa) and good tensile ductility (9.5 ± 1.4%) were achieved in the as-printed condition corresponding to DA = 0.5 mm. The tensile fracture surface features were analyzed and correlated to the influence of the DA values.
|
|---|