| Summary: | Formation of natural patina on copper and copper alloys objects takes tens of years. There are solutions for patination, which are used in restorers’ practice. However, these artificial patinas are usually based on nitrates, carbonates or chlorides. Patina based on brochantite is the most stable phase under atmospheric conditions. This type of patina was successfully formed in laboratory in a small exposure chamber with higher content of SO2. This work is next step of the experiment to make this method become more practicable. It started with construction 2 m3 exposure chamber and simulation of ideal conditions for patination process. The length of drying phase, homogeneity of conditions, pH of feeding water, colour of patina, placement of samples and final appearance were observed. The chamber construction allows to achieve ideal pH value of feeding water, samples surface became dry during the ventilation and temperature during condensation was stable at 40 °C. These conditions are ideal for patination process.
|
|---|