Multi-cycle rolled aluminum alloy 3103 sandwiches: mechanical properties and stamp ability
Constructional part producing by sheet stamping of multilayer composites requires the stamping ability data. The aim of a work is to estimate mechanical properties, stamping ratio and anisotropy indexes of 2, 4, 8 and 12 layer sandwiches produced from aluminium alloy AA3103. The pieces were received...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2017-01-01
|
| Series: | MATEC Web of Conferences |
| Online Access: | https://doi.org/10.1051/matecconf/201712902021 |
| Summary: | Constructional part producing by sheet stamping of multilayer composites requires the stamping ability data. The aim of a work is to estimate mechanical properties, stamping ratio and anisotropy indexes of 2, 4, 8 and 12 layer sandwiches produced from aluminium alloy AA3103. The pieces were received by the cold rolling. Interoperation annealing was at 500°C for 1 hour. Charts of tensile strength, yield stress, elongation depending on layer thickness were composed. It was found that cold strain hardening does not disappear after annealing if the foil’s thickness become 0.4 mm and less. Microstructure analysis has shown a good contact between layers for all samples and thicker outer layers. |
|---|---|
| ISSN: | 2261-236X |