Study on the Effect of Heat Treatment on Physical Properties of Poplar and Beech Woods Impregnated with Nano-Copper and Nano-Silver

• Main Authors: Hassan Siahposht, Maryam Ghorbani, Hamidreza Taghiyari
• Format: Article
• Language: fas
• Published: Iranian Scientific Association of Wood and Paper Industries 2012-06-01
• Series: Iranian Journal of Wood and Paper Industries
• Subjects: Heat treatment; Physical properties; Nano-Silver; Nano-Copper; Poplar; Beech
• Online Access: http://www.ijwp.ir/article_11469_cb2f7fb297a4f890c8d72907f996edc4.pdf

Present study conducted to review effects of heat treatment on weight loss, water adsorption, and thickness swelling of poplar (Populus nigra) and beech (Fagus oreintalis) woods impregnated with nano-copper and nano-silver. Specimens werepressur (2.5 bar) impregnated with 400 PPM water-based solution of nano-copper and nano-silver particles in a pressure vessel. For heat treatment, nano-cupper,  nano-silver impregnated and control specimens, were heat treated at 145°C temperature for 24 hours. Water absorption and thickness swelling decreased in heat treated and nano-heat treated specimens and this decrease in specimens impregnated with nano-copper and nano-silver was more obvious than in heat treated control specimens. The reasons were the degradation in crystal sections of celluloses chains and the ink variation of wood polymers. On the other hand, a comparison between heat treated and nano- heat treated specimens has shown weight loss further in nano-heat treated specimens. This shows that retent nano-copper and nano-silver by impregnation facilitates heat transfer in wood; and it may increase the process of degradation and pyrolysis of wood structures in inner parts of specimens.