THE INFLUENCE OF A HALLOYSITE ADDITIVE ON THE PERFORMANCE OF AUTOCLAVED AERATED CONCRETE
This paper presents the results from the tests of autoclaved aerated concrete with halloysite as a cement additive. Good pozzolanic properties make it a suitable material to be used as a partial replacement of a portion of cement. Basic physical and mechanical properties of the composites with vario...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Chemistry and Technology, Prague
2015-03-01
|
| Series: | Ceramics-Silikáty |
| Subjects: | |
| Online Access: |
http://www.ceramics-silikaty.cz/2015/pdf/2015_01_024.pdf
|
| Summary: | This paper presents the results from the tests of autoclaved aerated concrete with halloysite as a cement additive. Good pozzolanic properties make it a suitable material to be used as a partial replacement of a portion of cement. Basic physical and mechanical properties of the composites with various mineral content are discussed. The compressive strength test results indicate an increase in strength of the AAC containing 2.5 % and 5 % halloysite relative to the reference specimen. Thermal conductivity and density values remained at the same level. Observations of the microstructure in the scanning electron microscope confirmed the results from the XRD tests. Anhydrite was observed in addition to tobermorite. The results from the tests of the autoclaved aerated concretes in which halloysite was incorporated as 7.5 % and 10 % cement replacement showed an increase in compressive strength, density and thermal conductivity values. |
|---|---|
| ISSN: | 0862-5468 1804-5847 |