Facile Preparation of Highly Stretchable and Recovery Peptide-Polyurethane/Ureas

• Main Authors: Lin Gu, Yuanzhang Jiang, Jinlian Hu
• Format: Article
• Language: English
• Published: MDPI AG 2018-06-01
• Series: Polymers
• Subjects: polyurethane/urea; poly(γ-benzyl-l-glutamate); β-sheet conformation; shape recovery
• Online Access: http://www.mdpi.com/2073-4360/10/6/637

In this work, a new class of highly stretchable peptide-polyurethane/ureas (PUUs) were synthesized containing short β-sheet forming peptide blocks of poly(γ-benzyl-l-glutamate)-b-poly(propylene glycol)-b-poly(γ-benzyl-l-glutamate) (PBLG-b-PPG-b-PBLG), isophorone diisocyanate as the hard segment, and polytetramethylene ether glycol as the soft phase. PBLG-b-PPG-b-PBLG with short peptide segment length (<10 residues) was synthesized by amine-initiated ring opening polymerization of γ-benzyl-l-glutamate-N-carboxyanhydrides (BLG-NCA), which shows mixed α-helix and β-sheet conformation, where the percent of β-sheet structure was above 48%. Morphological studies indicate that the obtained PUUs show β-sheet crystal and nanofibrous structure. Mechanical tests reveal the PUUs display medium tensile strength (0.25–4.6 MPa), high stretchability (>1600%), human-tissue-compatible Young’s modulus (226–513 KPa). Furthermore, the shape recovery ratio could reach above 85% during successive cycles at high strain (500%). In this study, we report a facile synthetic method to obtain highly stretchable and recovery peptide-polyurethane/urea materials, which will have various potential applications such as wearable and implantable electronics, and biomedical devices.