| Summary: | We present a detailed investigation of the surface characteristics of five commercial titanium implants with different surface finishing (double acid etching, anodization and incorporation of Ca/P, acid etching and deposition of Ca/P, hydroxyapatite-blasting, acid etching and Ca/P-blasting) produced by five different manufacturers. A set of experimental techniques were employed to study the surface chemical composition and morphology: XPS, XRD, SEM, EDS, and AFM. According to the implat manufacturers, the addition of Ca and P at the implant surface is a main feature of these implants (except the double acid etched implant, which was included for comparative purpose). However, the results showed a great discrepancy on the final amount of these elements on the implant surface, which suggests a different effectiveness of the employed surface finishing methods to fix those elements on the implant surface. Our results show that only the method used by the manufacturer of hydroxyapatite-blasting surface finished implants was efficient to produce a hydroxyapatite coating. This group also showed the highest roughness parameters.
|
|---|