| Summary: | In the past decade, biomimetic calcium phosphate (CaP) ceramics have been considered as practicable grafts and biomaterial substitutes in repairing jaw bone defect after tumor resection or traffic accident. Nowadays, increasing incidence of biomedical material-associated infection has raised a concern when applying these materials. In this work, a new porous CaP scaffold with antibacterial coating was proposed. This biomimetic scaffold was composited with berberine (BBR), Ag nanoparticles (nAg), and silk fibroin (SF). The microstructures and phase composition of the scaffolds were analyzed. The cytocompatibility and osteogenic potential of the prepared samples were evaluated in vitro. The scaffolds held hierarchical structure: the first-level porous CaP ceramic with micron pores ranged from 250 to 600 µm; the second-level spongy-like structure with abundant capillary pores ranged from 500 nm to 10 µm; and the third-level structure was achieved by filling BBR, nAg, and SF gel coatings into the above porous structures. The experimental results showed that the antimicrobial capability of single BBR coating is inconspicuous. However, the introduction of nAg could significantly promote the antibacterial effect of scaffolds. At the same time, such scaffolds showed improved osteoinductivity. This new biomimetic CaP scaffold with antibacterial and osteoinductive properties may be a promising candidate for bone tissue engineering.
|
|---|