PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING

PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING

The growth of PbTiO3 ferroelectric thin films have successfully done. Thin films were made from bulk (powder) PbTiO3 dissolved in methanol solution. The condensation was mixed during 1 hour to get homogeneous condensation. Thin films were grown above corning substrates by spin coating method. Optima...

Full description

Bibliographic Details
Main Author: Bilalodin
Format: Article
Language:English
Published: Jenderal Soedirman University 2008-05-01
Series:Molekul
Subjects:
PbTiO3 thin film
spin coating method
characterization EDS
XRD and SEM
Online Access:http://www.jmolekul.com/?download=3.1.48.pdf
id doaj-1ad00446966d4c51bda7e811eff6aba7
record_format Article
spelling doaj-1ad00446966d4c51bda7e811eff6aba72020-11-24T20:40:34ZengJenderal Soedirman UniversityMolekul1907-97611907-97612008-05-01314852PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATINGBilalodin0Program Studi Fisika, Jurusan MIPA Fakultas Sains dan Teknik Universitas Jenderal Soedirman PurwokertoThe growth of PbTiO3 ferroelectric thin films have successfully done. Thin films were made from bulk (powder) PbTiO3 dissolved in methanol solution. The condensation was mixed during 1 hour to get homogeneous condensation. Thin films were grown above corning substrates by spin coating method. Optimation was done by various of annealing temperature. The physical properties of thin films were characterized by Energi Dispersive X-Ray Spectroscopy (EDS), X-Ray Diffraction (XRD), Scanning and Electron Microscopy (SEM). EDS measurement showed that the stoichiometry composition ratio of Pb/Ti is 1/1.26 at annealing temperature 600oC and 1/1.29 at annealing temperature 700oC. The result of XRD pattern showed that crystal structure of PbTiO3 thin films are tetragonal. The calculated lattice parameters ontained from Chohen Method arehttp://www.jmolekul.com/?download=3.1.48.pdfPbTiO3 thin filmspin coating methodcharacterization EDSXRD and SEM
collection DOAJ
language English
format Article
sources DOAJ
author Bilalodin
spellingShingle Bilalodin
PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING
Molekul
PbTiO3 thin film
spin coating method
characterization EDS
XRD and SEM
author_facet Bilalodin
author_sort Bilalodin
title PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING
title_short PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING
title_full PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING
title_fullStr PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING
title_full_unstemmed PENUMBUHAN DAN KARAKTERISASI LAPISAN TIPIS PbTiO3 YANG DISIAPKAN DENGAN TEKNIK SPIN COATING
title_sort penumbuhan dan karakterisasi lapisan tipis pbtio3 yang disiapkan dengan teknik spin coating
publisher Jenderal Soedirman University
series Molekul
issn 1907-9761
1907-9761
publishDate 2008-05-01
description The growth of PbTiO3 ferroelectric thin films have successfully done. Thin films were made from bulk (powder) PbTiO3 dissolved in methanol solution. The condensation was mixed during 1 hour to get homogeneous condensation. Thin films were grown above corning substrates by spin coating method. Optimation was done by various of annealing temperature. The physical properties of thin films were characterized by Energi Dispersive X-Ray Spectroscopy (EDS), X-Ray Diffraction (XRD), Scanning and Electron Microscopy (SEM). EDS measurement showed that the stoichiometry composition ratio of Pb/Ti is 1/1.26 at annealing temperature 600oC and 1/1.29 at annealing temperature 700oC. The result of XRD pattern showed that crystal structure of PbTiO3 thin films are tetragonal. The calculated lattice parameters ontained from Chohen Method are
topic PbTiO3 thin film
spin coating method
characterization EDS
XRD and SEM
url http://www.jmolekul.com/?download=3.1.48.pdf
work_keys_str_mv AT bilalodin penumbuhandankarakterisasilapisantipispbtio3yangdisiapkandenganteknikspincoating
_version_ 1716826474978213888

Similar Items