| Summary: | Blending polypropylene (PP) with thermoplastic elastomer SEBS can effectively improve the mechanical toughness of PP, thus leading to the promise of SEBS/PP as the primary insulation material for high voltage alternating current (HVAC) cables. However, the growth of electrical trees during cable operation limits the application of SEBS/PP. In this paper, acetylation reaction is used to construct acetophenone group at the end of the benzene ring on SEBS so that it has the effect of both a toughening agent and a voltage stabilizer. Then PP was melt blended with acetylated SEBS (Ac-SEBS), and the effects of Ac-SEBS on the mechanical properties, electrical tree resistance, alternating current (AC) breakdown strength, and dielectric spectrum of PP were mainly investigated with reference to PP and SEBS/PP. The results showed that Ac-SEBS with 30% content could enhance the mechanical toughness of PP and improve the electrical tree resistance and AC breakdown strength of SEBS/PP. The AC breakdown field strength of Ac-SEBS/PP reached the highest when the acetylation level was 4.6%, which was 9.2% higher than that of SEBS/PP. At this time, Ac-SEBS was also able to absorb high-energy electrons through the keto-enol interchange isomerization reaction, which inhibited the initiation and growth of electric trees and caused the development of electric dendrites in a jungle-like manner. Moreover, the dielectric loss factor of AC-SEBS/PP in power frequency is within the allowable range of industry. Therefore, Ac-SEBS/PP is expected to be applied to HVAC cables, thus further improving the efficiency of HVAC power transmission.
|
|---|