Well-Shaped Sulfonic Organosilica Nanotubes with High Activity for Hydrolysis of Cellobiose

• Main Authors: Jing Sun, Xiao Liu, Xinli Zhu, Hua Wang, Sadegh Rostamnia, Jinyu Han
• Format: Article
• Language: English
• Published: MDPI AG 2017-04-01
• Series: Catalysts
• Subjects: sulfonic solid acid catalysts; organosilica nanotubes; hydrolysis of cellobiose; acid density
• Online Access: http://www.mdpi.com/2073-4344/7/5/127
• ISSN: 2073-4344

Sulfonic organosilica nanotubes with different acidity densities could be synthesized through the co-condensation of ethenyl- or phenylene-bridged organosilane and 3-mercaptopropyltrimethoxysilane followed by sulfhydryl (–SH) oxidation. Transmission electron microscopy (TEM) analysis and nitrogen adsorption-desorption experiment clearly exhibit the hollow nanotube structures with the diameters of about 5 nm. The compositions of the nanotube frameworks are confirmed by solid state 13C nuclear magnetic resonance (NMR) while X-ray photoelectron spectroscopy (XPS) shows that about 60–80% of SH groups were oxidized to sulfonic acid (SO3H). The acid contents were measured by both elemental analysis (CHNS mode) and acid-base titration experiment, which revealed that the acid density was in the range of 0.74 to 4.37 μmol·m−2 on the solid. These nanotube-based acid catalysts exhibited excellent performances in the hydrolysis of cellobiose with the highest conversion of 92% and glucose selectivity of 96%. In addition, the catalysts could maintain high activity (65% conversion with 92% selectivity) even after six recycles.