A Study on Tensile Strain Distribution and Fracture Coordinate of Nanofiber Mat by Digital Image Correlation System

Strain gauges are commonly used for tension tests to obtain the strain of a metal test specimen. They make contact, however, so the gauges are not applicable to every type of test specimen. That is the reason why a non-contact type measurement system is required. Nanofibrous mats, manufactured by el...

Full description

Bibliographic Details
Main Authors: Nak Gyu Park, Kyung Min Hong, Kyu Hyeung Kwon
Format: Article
Language:English
Published: MDPI AG 2020-08-01
Series:Applied Sciences
Subjects:
Online Access:https://www.mdpi.com/2076-3417/10/17/5992
Description
Summary:Strain gauges are commonly used for tension tests to obtain the strain of a metal test specimen. They make contact, however, so the gauges are not applicable to every type of test specimen. That is the reason why a non-contact type measurement system is required. Nanofibrous mats, manufactured by electrospinning, have different structures and thicknesses. Displacement and strain distributions for all ranges of the specimen have never been demonstrated for nanofiber mats so far. Wrinkled nanofibrous mats of polyurethane were made and then tension-tested. The Digital Image Correlation (DIC) method was employed to measure displacement, then to calculate strain for all areas of the specimen. The DIC system consisted of a CMOS camera, control PC and operating software with a DIC algorithm: then, the Center of Gravity (COG) algorithm was used for this system. A cross-head speed of 3 mm/min was set for the tension test. The image record speed was one frame a second. In total, 400 image frames were obtained from the start, and then displacement and strain distributions were acquired for a 400 second tension test. The strain distribution from DIC system showed good agreement with the test result by a universal testing machine.