Synthesis, characterization and photoluminescence properties of Tm3+-doped Ca2YTaO6 blue-emitting phosphors
A series of Ca2YTaO6: Tm3+ blue-emitting phosphors were firstly prepared by the solid-state method. The phase formations and purity of Ca2YTaO6: xTm3+ (x = 0.3%-5% mol) were verified by X-ray powder diffraction. The morphological characteristics of Ca2YTaO6: 0.005Tm3+ were detected by scanning elect...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
EDP Sciences
2021-01-01
|
| Series: | E3S Web of Conferences |
| Online Access: | https://www.e3s-conferences.org/articles/e3sconf/pdf/2021/43/e3sconf_icsce2021_02018.pdf |
| Summary: | A series of Ca2YTaO6: Tm3+ blue-emitting phosphors were firstly prepared by the solid-state method. The phase formations and purity of Ca2YTaO6: xTm3+ (x = 0.3%-5% mol) were verified by X-ray powder diffraction. The morphological characteristics of Ca2YTaO6: 0.005Tm3+ were detected by scanning electron microscopy (SEM). Photoluminescence properties were discussed by emission (λem = 460 nm) and excitation (λex = 359 nm) spectra. The critical doping concentration of the products was 0.005 mol. The proposed concentration quenching mechanism in Ca2YTaO6 materials was the electric multipole interaction. Besides, the color coordinates (0.1408, 0.0891) of Ca2YTaO6: 0.005Tm3+ were located in blue region. The results suggested the Ca2YTaO6: Tm3+ phosphors can be promising blue-emitting components for the WLED applications. |
|---|---|
| ISSN: | 2267-1242 |