The micro-mechanisms of failure of nodular cast iron
The contribution deals with a comparison of the micro-mechanisms of failure of nodular cast irons at static, impact and fatigue stress. Several specimens of ferrite-pearlitic nodular cast irons with different content of ferrite in a matrix were used for metallographic analysis, mechanical tests and...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Printing House The Managers of Quality and Production Association
2014-12-01
|
| Series: | Production Engineering Archives |
| Subjects: | |
| Online Access: | http://www.qpij.pl/en/attachment/id/326 |
| Summary: | The contribution deals with a comparison of the micro-mechanisms of failure of nodular cast irons at static, impact and fatigue stress. Several specimens of ferrite-pearlitic nodular cast irons with different content of ferrite in a matrix were used for metallographic analysis, mechanical tests and micro-fractographic analysis. Mechanical properties were found by static tensile test, impact bending test and fatigue tests. The micro-fractographic analysis was made with use of scanning electron microscope VEGA II LMU on fracture surfaces of the specimens fractured by these mechanical and fatigue tests. Fracture surfaces of analysed specimens are characteristic of mixed mode of fracture. Micro-mechanism of failure of nodular cast irons is dependent on the method of stress. |
|---|---|
| ISSN: | 2353-5156 2353-7779 |