The effect of long-term thermal treatment on fatigue life of bimetal zirconium-steel
The paper describes the structure, mechanical properties and fatigue cracks growth in explosively welded zirconium – carbon steel cladding system subjected to long-lasting temperature impact. After annealing at 600 °C for 10 and 100 hours the samples were subjected to microscopic observations and f...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Publishing Agency - Welding Technology Review
2018-04-01
|
| Series: | Przegląd Spawalnictwa |
| Subjects: | |
| Online Access: | http://www.pspaw.pl/index.php/pspaw/article/view/876 |
| Summary: | The paper describes the structure, mechanical properties and fatigue cracks growth in explosively welded zirconium – carbon steel cladding system subjected to long-lasting temperature impact. After annealing at 600 °C for 10 and 100 hours the samples were subjected to microscopic observations and finally the microhardness, tensile strength and cyclic bending were determined. In the deformed specimens the initiation of fatigue cracks occurred in the steel whereas further cracks growth occurred parallel to the applied load.
in polish
Wpływ długotrwałej obróbki cieplnej na trwałość zmęczeniową bimetalu cyrkon-stal
W pracy opisano strukturę, właściwości mechaniczne oraz rozwój pęknięć zmęczeniowych w układach platerów cyrkon-stal zgrzewanych wybuchowo, poddanych długotrwałemu oddziaływaniu temperatury. Próbki w stanie po spojeniu wygrzewano w temperaturze 600 °C w czasie 10 i 100 godzin, a następnie poddano obserwacjom mikroskopowym, określono twardość, wytrzymałość na rozciąganie oraz poddano wahadłowemu zginaniu. W odkształconych próbkach zaobserwowano wzrost pęknięć zmęczeniowych równolegle do przyłożonego obciążenia, przy czym inicjacja pęknięć występowała w stali.
|
|---|---|
| ISSN: | 0033-2364 2449-7959 |