KARAKTERISTIK MIKROSTRUKTUR DAN FASA PADUAN Zr- 0,3%Nb-0,5%Fe-0,5%Cr PASCA PERLAKUAN PANAS DAN PENGEROLAN DINGIN

• Main Authors: Sungkono Sungkono, Masrukan Masrukan
• Format: Article
• Language: English
• Published: Pusat Teknologi Bahan Bakar Nuklir 2015-07-01
• Series: Urania
• Online Access: http://jurnal.batan.go.id/index.php/urania/article/view/2262
• ISSN: 0852-4777; 2528-0473

KARAKTERISTIK MIKROSTRUKTUR DAN FASA PADUAN Zr-0,3%Nb-0,5%Fe-0,5%Cr PASCA PERLAKUAN PANAS DAN PENGEROLAN DINGIN. Logam paduan Zr-Nb-Fe-Cr dikembangkan sebagai material kelongsong elemen bakar dengan fraksi bakar tinggi untuk reaktor daya maju. Dalam penelitian ini telah dibuat paduan Zr-0,3%Nb-0,5%Fe-0,5%Cr yang mendapat perlakuan panas pada temperatur 650 dan 750°C dengan waktu penahanan 1–2 jam. Tujuan penelitian adalah mendapatkan karakter paduan Zr-0,3%Nb-0,5%Fe-0,5%Cr pasca perlakuan panas dan pengerolan dingin yaitu mikrostruktur, struktur kristal dan fasa-fasa yang ada dalam paduan. Hasil penelitian menunjukkan bahwa paduan Zr-0,3%Nb-0,5%Fe-0,5%Cr pasca perlakuan panas (650ºC, 1-2 jam) mempunyai struktur butir ekuiaksial dengan ukuran butir bertambah besar seiring dengan bertambahnya waktu penahanan. Sementara itu, pasca perlakuan panas (750ºC, 1-2 jam) terjadi perubahan mikrostruktur paduan dari butir ekuiaksial dan kolumnar menjadi butir ekuiaksial lebih besar. Paduan Zr-0,3%Nb-0,5%Fe-0,5%Cr pasca perlakuan panas (650°C, 1 jam) dan (750°C, 1 jam) tidak dapat dirol dingin dengan reduksi tebal 5 – 10%, sedangkan pasca perlakuan panas (650ºC, 2 jam) dan (750°C, 1.5-2 jam) mampu menerima deformasi dingin dengan reduksi ketebalan 5-10% tanpa mengalami keretakan. Senyawa Zr2Fe, ZrCr2 dan FeCr teridentifikai dari hasil uji kristalografi paduan Zr-0,3%Nb-0,5%Fe-0,5%Cr.   MICROSTRUCTURE AND PHASE CHARACTERISTICSOF Zr-0.3%Nb-0.5%Fe-0.5%Cr ALLOY POST HEAT TREATMENT AND COLD ROLLING. Zr-Nb-Fe-Cr alloys was developed as fuel elements cladding with high burn up for advanced power reactors. In this research has been made of Zr-0.3% Nb-0.5% Fe-0.5% Cr alloy were heat treated with varying temperatures at650 and 750°C for 1 until 2 hours. The objectives of this research was to obtain the character of Zr-0.3% Nb-0.5% Fe-0.5% Cr alloy post heat treatment and cold rolling, microstructure nomenclature, crystal structure and phases that presents in the alloy. The results of this experiment showed that the microstructures of Zr-0.3% Nb-0.5% Fe-0.5% Cr alloy post heat treatment (650ºC, 1-2 hours) had equiaxial grain structure with an enlarged size with increasing of the retention time. Meanwhile, post heat treatment (750°C, 1-2 hours) occurred the microstructures evolution of alloy from equiaxial and columnar became equiaxial and columnar relatively large, and subsequently became the larger equiaxial grains. Zr-0.3% Nb-0.5% Fe-0.5% Cr alloy post heat treatment (650°C, 2 h) and (750°C, 1.5-2 hours) can undergo cold deformation without cracking when thickness reduction between 5 to 10%.The phases formation of Zr2Fe, ZrCr2 and FeCr compounds can improve the mechanical strength and the corrosion resistance of Zr-0.3% Nb-0.5% Fe-0.5% Cr alloy.