Behavioral Analysis of Hydrogen in Metals under the Effect of H2S Corrosion Using a Layer-stripping Micro-hardness Technique
In order to study the distribution behavior of hydrogen in metals under the condition of H2S corrosion, a layer-stripping micro-hardness test was designed to analyze the hydrogen distribution along the depth of hydrogen-charged 45 high-quality structural carbon steel at three different hydrogen sulf...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Kaunas University of Technology
2020-02-01
|
| Series: | Medžiagotyra |
| Subjects: | |
| Online Access: | http://matsc.ktu.lt/index.php/MatSc/article/view/22103 |
| Summary: | In order to study the distribution behavior of hydrogen in metals under the condition of H2S corrosion, a layer-stripping micro-hardness test was designed to analyze the hydrogen distribution along the depth of hydrogen-charged 45 high-quality structural carbon steel at three different hydrogen sulfide concentrations and four corrosion periods in this study. The results show that there is a terminal solid solubility of hydrogen in the metal for hydrogen sulfide solutions over various concentrations and corrosion periods. A hydrogen-saturated layer is produced by hydrogen diffusing through the metal from an unsaturated state to a fully saturated state. The hydrogen-saturated layer is not affected by the concentration of the corrosion, but its thickness increases as the corrosion period increases. In this way, we established a new hydrogen diffusion model in metals. |
|---|---|
| ISSN: | 1392-1320 2029-7289 |