Enhanced Corrosion Resistance of SA106B Low-Carbon Steel Fabricated by Rotationally Accelerated Shot Peening
The corrosion resistance of a SA106B carbon steel with a gradient nanostructure fabricated by rotationally accelerated shot peening (RASP) for 5, 10, 15 and 20 min was investigated. Electrochemical tests were carried out in the 0.05 M H<sub>2</sub>SO<sub>4</sub> + 0.05 M Na&l...