Effect of pre-etching on sealing ability of two current self-etching adhesives
Background: We evaluated the effect of phosphoric acid etching on microleakage of two current self-etching adhesives on enamel margins in comparison to a conventional total- etch system. Methods: Sixty buccal class V cavities were made at the cemento-enamel junction with beveled enamel marg...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wolters Kluwer Medknow Publications
2005-05-01
|
| Series: | Journal of Research in Medical Sciences |
| Online Access: | http://journals.mui.ac.ir/jrms/article/view/127 |
| Summary: | Background: We evaluated the effect of phosphoric acid etching on microleakage of two current self-etching adhesives on enamel margins in comparison to a conventional total- etch system. Methods: Sixty buccal class V cavities were made at the cemento-enamel junction with beveled enamel margins of extracted human premolar teeth and randomly divided into five groups (12 specimens in each group). Group 1 was applying with Clearfil SE bond, Group 2 with 35% phosphoric acid etching of enamel margins plus Clearfil SE bond, Group3 with I bond, Group 4 with 35% phosphoric acid etching of enamel margins plus I bond and Group5 with Scotchbond multi-purpose. All groups restored with a composite resins. After 24 hours storage with 100% humidity, the samples were thermocycled, immersed in a dye solution and sectioned buccoligually and enamel margins microleakage were evaluated on a scale of 0 to 2. Results: The differences between Groups 1 & 3 and Groups 3 & 4 were significant (P<0.05) but no significant differences between Groups1 & 2 or 1 & 5 were observed. Conclusion: The findings suggest that all-in-one adhesive systems need pre-etching enamel margins with phosphoric acid for effectively seal. Key words: Self-Etching Adhesives, Microleakage, Enamel, Total-Etch system |
|---|---|
| ISSN: | 1735-1995 1735-7136 |