Fatigue of Micro Molded Materials - Aluminum Bronze and Yttria Stabilized Zirconia
Custom built setups were developed to investigate micro samples during quasistatic and cyclic testing in tension, compression and bending. Micro molded CuAl10Ni5Fe4-samples showed similar fatigue behavior compared to macroscopic samples due to both the sample size and microstructure being scaled dow...
| Format: | eBook |
|---|---|
| Language: | English |
| Published: |
KIT Scientific Publishing
2014
|
| Series: | Schriftenreihe des Instituts für Angewandte Materialien, Karlsruher Institut für Technologie
|
| Subjects: | |
| Online Access: | Open Access: DOAB: description of the publication Open Access: DOAB, download the publication |
| LEADER | 02044namaa2200385uu 4500 | ||
|---|---|---|---|
| 001 | doab47440 | ||
| 003 | oapen | ||
| 005 | 20210211 | ||
| 006 | m o d | ||
| 007 | cr|mn|---annan | ||
| 008 | 210211s2014 xx |||||o ||| 0|eng d | ||
| 020 | |a 9783731502937 | ||
| 020 | |a KSP/1000043832 | ||
| 024 | 7 | |a 10.5445/KSP/1000043832 |2 doi | |
| 040 | |a oapen |c oapen | ||
| 041 | 0 | |a eng | |
| 042 | |a dc | ||
| 072 | 7 | |a TB |2 bicssc | |
| 720 | 1 | |a Kennerknecht, Tobias |4 aut | |
| 245 | 0 | 0 | |a Fatigue of Micro Molded Materials - Aluminum Bronze and Yttria Stabilized Zirconia |
| 260 | |b KIT Scientific Publishing |c 2014 | ||
| 300 | |a 1 online resource (XII, 255 p. p.) | ||
| 336 | |a text |b txt |2 rdacontent | ||
| 337 | |a computer |b c |2 rdamedia | ||
| 338 | |a online resource |b cr |2 rdacarrier | ||
| 490 | 1 | |a Schriftenreihe des Instituts für Angewandte Materialien, Karlsruher Institut für Technologie | |
| 506 | 0 | |a Open Access |f Unrestricted online access |2 star | |
| 520 | |a Custom built setups were developed to investigate micro samples during quasistatic and cyclic testing in tension, compression and bending. Micro molded CuAl10Ni5Fe4-samples showed similar fatigue behavior compared to macroscopic samples due to both the sample size and microstructure being scaled down with the manufacturing process. Results from cyclic three-point bending tests on micro molded 3Y-TZP suggested that a minimum crack extension is necessary to develop cyclically degradable shielding. | ||
| 540 | |a Creative Commons |f https://creativecommons.org/licenses/by-sa/4.0/ |2 cc |u https://creativecommons.org/licenses/by-sa/4.0/ | ||
| 546 | |a English | ||
| 650 | 7 | |a Technology: general issues |2 bicssc | |
| 653 | |a Ermüdung Mikroguss Aluminiumbronze Zirkonoxid Apparaturresonance custom-built setup microstructure 3Y-TZP | ||
| 793 | 0 | |a DOAB Library. | |
| 856 | 4 | 0 | |u https://directory.doabooks.org/handle/20.500.12854/47440 |7 0 |z Open Access: DOAB: description of the publication |
| 856 | 4 | 0 | |u https://www.ksp.kit.edu/9783731502937 |7 0 |z Open Access: DOAB, download the publication |